Steelshot is produced in a melting process and then transformed into steel balls in the atomization process. Thanks to the high hardness the steel shot achieves high blast intensity already from the beginning in the blasting process. We also offer steel shot according to standardized specifications, for example AMS 2431. Please inquire about the possibilities. Download datasheet
| Quantity | Discount | Price per kg |
|---|---|---|
| 25 – 475 kg | – | € 1.75 |
| 500 – 975 kg | 12% | € 1.55 |
| 1,000 – 2,975 kg | 36% | € 1.129 |
| 3,000 – 4,975 kg | 37% | € 1.112 |
| 5,000 kg and more | 37% | € 1.101 |
| Displayed prices include all applicable surcharges (scrap, energy, sea freight and gas surcharge, depending on the product type). | ||
| Quantity | Discount | Price per kg |
|---|---|---|
| 1 – 499 kg | - | € 2.33 |
| 500 – 999 kg | 9% | € 2.11 |
| 1,000 – 2,999 kg | 29% | € 1.652 |
| 3,000 – 4,999 kg | 30% | € 1.634 |
| 5,000 kg and more | 30% | € 1.623 |
| Displayed prices include all applicable surcharges (scrap, energy, sea freight and gas surcharge, depending on the product type). | ||
| Properties | Values |
|---|---|
| Hardness | 40 – 52 HRC (390 – 535 HV) |
| Grain form | beef |
| Melting point | approx. 1,535 °C |
| Specific gravity | approx. 7 g/cm³ |
| Bulk density | approx. 4.0 – 4.6 g/cm³ |
| Mikrostrukture | martensitic |
| Component | Percent |
|---|---|
| C | 0,80 – 1,20 % |
| Mn | 0,35 – 1,20 % |
| Si | 0,40 – 1,50 % |
| S | max. 0.05 % |
| P | max. 0.05% |
| Fe | Rest |
| Designation | Nominal dimension (mm) |
|---|---|
| S 280 | 0,7 – 1,0 |
| S 330 | 0,9 – 1,2 |
| S 390 | 1,0 – 1,4 |
| S 460 | 1,2 – 1,7 |
| S 550 | 1,4 – 2,0 |
| S 660 | 1,7 – 2,2 |